TY - JOUR
T1 - A comparative study of spark plasma sintering and hybrid spark plasma sintering of 93W-4.9Ni-2.1Fe heavy alloy
AU - Shongwe, Mxolisi Brendon
AU - Diouf, Saliou
AU - Durowoju, Mondiu Olayinka
AU - Olubambi, Peter Apata
AU - Ramakokovhu, Munyadziwa Mercy
AU - Obadele, Babatunde Abiodun
N1 - Publisher Copyright:
© 2015 Elsevier Ltd. All rights reserved.
PY - 2016/2/1
Y1 - 2016/2/1
N2 - Mixed 93W-4.9Ni-2.1Fe powders were sintered via the spark plasma sintering (SPS) and hybrid spark plasma sintering (HSPS) techniques with 30 mm and 60 mm samples in both conditions. After SPS and HSPS, the 30 mm and 60 mm alloys (except 60 mm-SPS) had a relative density (> 99.2%) close to the theoretical density. Phase, microstructure and mechanical properties evolution of W-Ni-Fe alloy during SPS and HSPS were studied. The microstructural evolution of the 60 mm alloys varied from the edge of the sample to the core of the sample. Results show that the grain size and the hardness vary considerable from the edge to the core of sintered sample of 60 mm sintered using conventional SPS compared to hybrid SPS. Similarly, the hardness also increased from the edge to the core. Furthermore, the 60 mm-HSPS alloy exhibited improved bending strength of 1115 MPa when compared to that of 60 mm-SPS, 920 MPa. The intergranular fracture along the W/W grain boundary is the main fracture modes of W-Ni-Fe, however in the 60 mm-SPS alloy peeling of the grains was also observed which diminished the properties. The mechanical properties of SPS and HSPS 93W-4.9Ni-2.1Fe heavy alloys are dependent on the microstructural parameters such as tungsten grain size and overall homogeneity.
AB - Mixed 93W-4.9Ni-2.1Fe powders were sintered via the spark plasma sintering (SPS) and hybrid spark plasma sintering (HSPS) techniques with 30 mm and 60 mm samples in both conditions. After SPS and HSPS, the 30 mm and 60 mm alloys (except 60 mm-SPS) had a relative density (> 99.2%) close to the theoretical density. Phase, microstructure and mechanical properties evolution of W-Ni-Fe alloy during SPS and HSPS were studied. The microstructural evolution of the 60 mm alloys varied from the edge of the sample to the core of the sample. Results show that the grain size and the hardness vary considerable from the edge to the core of sintered sample of 60 mm sintered using conventional SPS compared to hybrid SPS. Similarly, the hardness also increased from the edge to the core. Furthermore, the 60 mm-HSPS alloy exhibited improved bending strength of 1115 MPa when compared to that of 60 mm-SPS, 920 MPa. The intergranular fracture along the W/W grain boundary is the main fracture modes of W-Ni-Fe, however in the 60 mm-SPS alloy peeling of the grains was also observed which diminished the properties. The mechanical properties of SPS and HSPS 93W-4.9Ni-2.1Fe heavy alloys are dependent on the microstructural parameters such as tungsten grain size and overall homogeneity.
UR - https://www.scopus.com/pages/publications/84946854571
UR - https://www.scopus.com/pages/publications/84946854571#tab=citedBy
U2 - 10.1016/j.ijrmhm.2015.11.001
DO - 10.1016/j.ijrmhm.2015.11.001
M3 - Article
AN - SCOPUS:84946854571
SN - 0263-4368
VL - 55
SP - 16
EP - 23
JO - International Journal of Refractory Metals and Hard Materials
JF - International Journal of Refractory Metals and Hard Materials
ER -