The effect of silicon doping and thermal annealing on the electrical and structural properties of hydrogenated amorphous carbon thin films

T. I.T. Okpalugo, P. D. Maguire, A. A. Ogwu, J. A.D. McLaughlin

Research output: Contribution to journalArticlepeer-review

39 Citations (Scopus)

Abstract

Silicon addition to a-C:H (hydrogenated amorphous carbon) thin films offers many advantages and a full understanding of the electrical properties of a-C:H:Si thin films is necessary for applications like biomedical implants and biosensor devices. The thin films were deposited with 13.56 MHz RF-PECVD (plasma enhanced chemical vapour deposition) using acetylene, argon and tetramethylsilane (TMS) vapour on p-type and n-type Si (100) wafers, and some of the films were further modified by thermal annealing. Silicon incorporation into a-C:H improves the thermal stability against graphitisation but decreases the film resistivity and breakdown strength. The breakdown strength variation is likely to be determined by inclusion of conductive clusters but the source of these clusters is unclear, since Raman indicates an increase in sp3 content. The contact potential difference (CPD) of a-C:H thin films decreased by (approx. 0.21-0.43 eV) with increasing annealing temperatures, due to reduction in bandgap towards graphite, and increasing amounts of silicon, suggesting a more p-type structure due to higher trap densities, although change in bandgap or surface charge may also play a role.

Original languageEnglish
Pages (from-to)1549-1552
Number of pages4
JournalDiamond and Related Materials
Volume13
Issue number4-8
DOIs
Publication statusPublished - Apr 2004
Externally publishedYes

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • General Chemistry
  • Mechanical Engineering
  • Materials Chemistry
  • Electrical and Electronic Engineering

Fingerprint

Dive into the research topics of 'The effect of silicon doping and thermal annealing on the electrical and structural properties of hydrogenated amorphous carbon thin films'. Together they form a unique fingerprint.

Cite this